Design guidelines for Osprey™ CE7 and CE9 alloys
Osprey™ CE7 and CE9 controlled expansion alloys exhibit attractive properties for many thermal management and electronic packaging components; such as low CTE, low density, high specific stiffness, thermal stability, flatness and high thermal conductivity. However, these materials are relatively brittle and therefore the design of components must be carefully controlled to achieve optimum results.
Generally, normal design rules for CNC machining should be followed for the CE alloys other than for those features covered by the guidelines below.
Avoid positioning holes very close to the side walls of packages and to the edges of tags or plates; e.g. allow at least a 1 mm wall surrounding the hole.
Threaded holes down to 0-80 UNC are possible to machine.
Bolting down of plates
Use a plain washer rather than a bush insert so as to prevent cracking (see below).
External radii are generally not required (although they can be machined with ease) and will add to cost, because 'starting' blocks are normally cut with square sides. Parts can be chamfered if necessary.
Large radii are desirable (e.g. 0.5 to 0.75 mm or greater) in order to reduce machining cost.
Minimize use of hold-down tags if possible. However, if tags are necessary, ensure that they are reasonably thick (>1mm), that they have large internal radii (typically >=3 mm) and are at least 3mm wider than the holes in the tags.
Generally, a thickness of walls/base >1 mm is recommended, although thinner walls can be incorporated provided that the wall height is <5 mm.