Sandvik SAF 2507® is a high alloy duplex (austenitic-ferritic) stainless steel for service in highly corrosive conditions. The grade is characterized by:
- Excellent resistance to stress corrosion cracking in chloride-bearing environments
- Excellent resistance to pitting and crevice corrosion
- High resistance to general corrosion
- Very high mechanical strength
- Physical properties that offer design advantages
- High resistance to erosion corrosion and corrosion fatigue good weldability
- Excellent mechanical properties that allow for lighter constructions, more compact design and less welding
EN Number: 1.4410
EN Name: X2CrNiMoN25-7-4
- EN 10088-3, (dimensions up to 160 mm)
- EN 10272, EN 10222-5
- ASTM A479, ASTM A276
- NORSOK MDS D57 Rev 4, Rev 5
- Suitable for manufacturing of components in accordance with ASTM A182
Pressure Equipment Directive (2014/68/EU)
NORSOK M650 Ed. 4, NORSOK M630 Ed. 6, dimensions up to 250 mm.
Pre-approval for PMA
Status according to EN 10 204/3.1
Chemical composition (nominal)
Sandvik SAF 2507® is a duplex stainless steel specially designed for service in aggressive chloride-containing environments. Typical applications are:
- Oil and gas industry
- Seawater cooling
- Salt evaporation industry
- Desalination plants
- Geothermal wells
- Refineries and petrochemical plants
- Mechanical components requiring high strength
- Pulp and paper industry
Sandvik SAF 2507® is highly resistant to corrosion by organic acids, e.g. formic and acetic acid. It is suitable for use at high concentrations and temperatures, where austenitic stainless steels corrode at a high rate.
Resistance to inorganic acids is comparable to that of high alloy austenitic stainless steels in certain concentration ranges.
Pitting and crevice corrosion
The pitting and crevice corrosion resistance of a stainless steel is primarily determined by the content of chromium, molybdenum and nitrogen. An index for comparing the resistance to pitting and crevice corrosion is the PRE number (Pitting Resistance Equivalent).
The PRE is defined as, in weight-% PRE = %Cr + 3.3 x %Mo + 16 x %N
For duplex stainless steels the pitting corrosion resistance is dependent on the PRE-value in both the ferrite phase and the austenite phase, so that the phase with the lowest PRE-value will be limiting for the actual pitting corrosion resistance. In Sandvik SAF 2507® the PRE-value is equal in both phases, which has been achieved by a careful balancing of the elements.
The minimum PRE-value for Sandvik SAF 2507® is 41. This is significantly higher than e.g. the PRE-values for other duplex stainless steels of the 25Cr type which are not "super-duplex". As an example UNS S31260 (25Cr3Mo0.2N) has a PRE-value of typically 38.
One of the most severe pitting and crevice corrosion tests applied to stainless steel is ASTM G48, i.e., exposure to 6% FeCl3 with and without crevices (method A and B respectively). When pits are detected following a 24 hours exposure, together with a substantial weight loss (>5 mg), the test is interrupted. Otherwise, the temperature is increased 5°C (9°F) and the test is continued with the same sample. Figure 4 shows critical pitting and crevice temperatures (CPT and CCT) from this test.
Figure 4. Critical pitting and crevice temperatures in 6% FeCl3. 24h (similar to ASTM G48).
Stress corrosion cracking
Sandvik SAF 2507® has excellent resistance to chloride-induced stress corrosion cracking.
Erosion corrosion and corrosion fatigue
The superior mechanical properties combined with the improved corrosion resistance of Sandvik SAF 2507® result in excellent resistance to both erosion corrosion and corrosion fatigue compared to standard austenitic stainless steels.
Forms of supply
Finishes and dimensions
Sandvik SAF 2507® bar steel is stocked in a large number of sizes. The standard size range for stock comprises 20-250 mm, see pocket card S-02909. Round bar is supplied in solution annealed and water quenched condition. The surface is peeled turned and polished.
Bars are delivered in random lengths of 3-7 m, depending on diameter.
|Height of arch, mm/m
|20 - 70||1|
|Diameter, mm||Tolerances, mm|
|Size, mm dia|
|Peeled and burnished||1||20-250|
Bars are normally delivered in solution annealed and quenched condition. Additional heat treatment, as recommended below is only needed if further hot working has been made.
Slow heating up to 1000°C (1830°F). Annealing at 1050-1125°C (1920-2060°F), followed by quenching.
Bar steel is tested in delivery condition.
The following figures apply to material in the solution annealed and quenched condition.
For small sections the proof strength values are higher than those listed below at 20 °C (68 °F).
More detailed information can be supplied on request.
At 20°C (68°F)
Metric units, bar
|Proof strength||Tensile strength||Elong.||HB|
Imperial units, bar
|Proof strength||Tensile strength||Elong.||Hardness|
1 MPa = 1 N/mm2
a) Rp0.2 corresponds to 0.2% offset yield strength.
b) Based on L0 = 5.65√S0 , where L0 is the original gauge length and S0 the original cross-section area.
c) For sizes below 50 mm/2" Rm min. 800 MPa.
At higher temperatures
If Sandvik SAF 2507® is exposed for prolonged periods to temperatures exceeding 250°C (480°F), the microstructure changes which results in a reduction in impact strength. This effect does not necessarily affect the behavior of the material at the operating temperature.
More detailed information can be supplied on request.
Sandvik SAF 2507® possesses good impact strength. Figure 2 shows typical impact energy values for Sandvik SAF 2507 in different sizes at -20°C (-4°F), using standard Charpy V specimens. Samples taken in the longitudinal direction.
The impact energy (Charpy V) at 20°C (68°F) is min 100 J (74 ft-lb).
Density: 7.8 g/cm3, 0.28 lb/in3
Specific heat capacity
Metric units, Imperial units
|Temperature, °C||J/(kg °C)||Temperature, °F||Btu/(lb °F)|
Metric units, W/(m °C)
Imperial units, Btu/(ft h °F)
Sandvik SAF 2507® has a coefficient of thermal expansion close to that of carbon steel. This gives Sandvik SAF 2507® definite design advantages over austenitic stainless steels in equipment comprising of both carbon steel and stainless steel. The values given below are average values in the temperature ranges.
Metric units, x10-6/°C
|Sandvik SAF 2507||13.5||14.0||14.0||14.5|
Imperial units, x10-6/°F
|Sandvik SAF 2507||7.5||7.5||8.0||8.0|
|Temperature, °C||μΩm||Temperature, °F||μΩin.|
Modulus of elasticity, (x103)
Metric units Imperial units
|Temperature, °C||MPa||Temperature, °F||ksi|
Being a two-phase material (austenitic-ferritic) Sandvik SAF 2507® will present a different wear picture from that of single-phase steels of type ASTM 304L. The cutting speed must therefore be lower than that recommended for ASTM 304L. It is recommended that a tougher insert grade is used than when machining austenitic stainless steels, e.g. ASTM 304L. Also in comparison with SANMAC® 2205 lower speed and tougher insert grade is recommended. Machining recommendations available on request. More cutting data information for Sandvik SAF 2507® is available in the product handbook S-02909-ENG, these recommendations could act as guidelines in choice of appropriate cutting data.
The weldability of Sandvik SAF 2507® is good. Suitable methods of fusion welding are manual metal-arc welding (MMA/SMAW) and gas-shielded arc welding, with the TIG/GTAW method as first choice.
For Sandvik SAF 2507®, heat input of 0.2-1.5 kJ/mm and interpass temperature of <150°C (300°F) are recommended. Preheating and post-weld heat treatment are normally not necessary.
Recommended filler metals
ISO 14343 S 25 9 4 N L / AWS A5.9 ER2594 (e.g. Exaton 25.10.4.L)
ISO 3581 E 25 9 4 N L R / AWS A5.4 E2594-16 (e.g. Exaton 25.10.4.LR)
ISO 3581 E 25 9 4 N L B / AWS A5.4 E2594-15 (e.g. Exaton 25.10.4.LB)