Sandvik 10C28Mo2 is a martensitic stainless chromium steel developed for razor blade and knife applications with high demands on corrosion resistance. The carefully chosen chemical composition in combination with a very fine microstructure also provides a high hardness, good edge retention, toughness and edges that are easy to re-sharpen.
After heat treatment the grade is characterized by:
- Very good corrosion resistance
- High hardness which gives good wear resistance
- Good toughness
Typical applications for Sandvik 10C28Mo2 are kitchen knives and other tools where a dishwasher-safe material is required, professional butcher knives that need to be easily re-sharpened, outdoor knives, medical blades and razor blades, with high requirements on corrosion resistance and toughness.
Chemical composition (nominal)
Forms of Supply
The strips can be supplied either in coils or as straightened lengths of 0.5 - 4.0 meter (1.6 - 13.1 feet). The coil weight is max 5 kg/mm (280 lbs/in.) of strip width.
Hardening and tempering of the strip steel is needed to achieve the correct finish and to meet the properties required by the end user.
|Thickness, mm (in.)||Width mm (in.)|
|0.074 (0.0029)||4.5 (0.177)||5 (0.197)||380 (14.96)|
Other sizes can be supplied to meet specific requirements.
The thickness and width tolerances are +/- tolerances to the nominal size. The normal tolerance classes for most of our strip products are T2 and B1. Tighter tolerances as well as other tolerance limits can be offered upon request.
The exact hardening parameters need to be adjusted in every individual furnace.
A general recommendation is given below:
To room temperature: Recommended temperature: 1050°C (1920°F)
Deep freezing to -70°C: Recommended temperature: 1070°C (1960°F)
Time in furnace according to table.
|Thickness (mm)||Thickness (in.)||Time (minutes)|
To room temperature: Recommended temperature: 1040°C (1900°F)
Deep freezing to -70°C: Recommended temperature: 1060°C (1940°F)
Soaking time 30 minutes in furnace.
The temperature should first be equalized at 850°C (1560°F) for 30 minutes to avoid necessary temperature variations.
Quench to room temperature as rapid as possible. For optimum results 600°C (1110°F) should be reached within 2 minutes or less.
It is recommended that tempering is performed between 175-350°C (345-660°F) for 2 hours. Below is an estimation of the hardness levels that can be expected with different tempering temperatures.
After quenching to room temperature:
|58 HRC||175°C (345°F)|
|56 HRC||225°C (435°F)|
|55 HRC||350°C (660°F)|
|60 HRC||175°C (345°F)|
|58 HRC||225°C (435°F)|
|56 HRC||350°C (660°F)|
|Condition||Tensile strength||Hardness 1)|
|Annealed||720 ± 100 (105 ± 14)||225 ± 35|
|Cold rolled||800 – 1200 (116 - 174)||240 - 360|
1) Hardness data is for guidance only.
The physical properties of a steel are related to a number of factors, including alloying elements, heat treatment and manufacturing route, but the data presented below can generally be used for rough calculations.
Density: 7.7 g/cm3 (0.28 lb/in3)