Sandvik SAF™ 2507 is a super-duplex (austenitic-ferritic) stainless steel for service in highly corrosive conditions. The grade is characterized by:
- Excellent resistance to stress corrosion cracking (SCC) in chloride-bearing environments
- Excellent resistance to pitting and crevice corrosion
- High resistance to general corrosion
- Very high mechanical strength
- Physical properties that offer design advantages
- High resistance to erosion corrosion and corrosion fatigue
- Good weldability
- UNS: S32750
- EN Number: 1.4410
- EN Name: X 2 CrNiMoN 25-7-4
Chemical composition (nominal) %
Forms of supply
The strip steel can be supplied in coils, bundles, on plastic spools or in lengths. The edges can be either slit, deburred or smoothly rounded.
Conditions and dimensions
Sandvik SAF™ 2507 is supplied in solution annealed (bright annealed or annealed
and pickled) or cold rolled condition.
2-300 mm (0.078-12 in.)
0.015-3.5 mm (0.0006-0.14 in.)
|Condition||Tensile strength, Rm||Proof strength, Rp0,2a)||Elongation, A11,3|
a) Rp0,2 corresponds to 0.2% offset yield strength.
1 MPa = N/mm2
A = Annealed
C = Cold rolled
CT = Cold rolled and aged, 480°C (896°F)/3 h (see further under section "Heat treatment".)
Nominal values at 20°C (68°F) in a normal dry atmosphere. The fatigue limit is defined as the stress at which 50% of the specimens withstand a minimum of 2 million load cycles.
Reversed bending stress
Average stress = 0
Bending transversal to rolling direction.
|Tensile strength, Rm||Fatigue limit, MPa||Tensile strength, Rm||Fatigue limit, ksi|
|Thickness, mm||Thickness, inch|
|1850||± 540||268||± 78|
The physical properties of a steel are related to a number of factors, including alloying elements, heat treatment and manufacturing process, but the following data can generally be used for rough calculations. The values refer to testing in the annealed condition at 20°C (68°F), where nothing else is mentioned.
Density: 7.8 g/cm3, 0.28 lb/in3
|Temperature, °C||W/m °C||Temperature, °F||Btu/ft h°F|
|Sandvik SAF 2507||8||9||9||10||12|
Specific heat capacity
|Temperature, °C||J/(Kg °C)||Temperature, °F||Btu/(lb °F)|
Sandvik SAF 2507® has a coefficient of thermal expansion close to that of carbon steel. This gives Sandvik SAF 2507® definite design advantages over austenitic stainless steels in equipment comprising of both carbon steel and stainless steel. The values given below are average values in the temperature ranges.
Sandvik SAF 2507
Carbon steel (0.2%C)
Sandvik SAF 2507
Carbon steel (0.2%C)
|Condition||Tensile strength, Rm, MPa||E, MPa||Tensile strength, Rm, ksi||E, ksi|
|Cold rolled and aged||1850||210||268||30.5|
Sandvik SAF™ 2507 is highly resistant to corrosion by organic acids, e.g. formic and acetic acid. Also in chloride contaminated acid the grade remains resistant.
Sandvik SAF™ 2507 in the annealed, cold rolled as well as cold rolled and aged condition has passed salt spray tests during 500 h according to ISO 9227:2006 without any attack.
The pitting corrosion resistance was assessed electrochemically by the method ASTM G150. The Critical Pitting Temperature (CPT) was measured with results according to the below table.
|Condition||Tensile strength, Rm, MPa||CPT, oC||CPT, oF|
|Cold rolled and aged (480oC/3h)||2000||>80||>176|
The recommended annealing cycle is 1050-1125°C (1920-2060°F) for 1-5 minutes, followed by rapid cooling in air or water.
The strength of cold rolled Sandvik SAF™ 2507 can be increased by a heat treatment operation at 480oC (900oF) for 3 h. An increase in tensile strength of 200-300 MPa and in proof strength of 400-500 MPa can be expected. Aging also increases the modulus of elasticity.
Aging is normally carried out after forming. If the aging is performed in an open air furnace, a brownish oxide is formed on the surface. To avoid discoloration, parts should be carefully cleaned before heat treatment.
The weldability of Sandvik SAF™ 2507 is good. Suitable welding methods are manual metal-arc welding with covered electrodes or gas shielded arc welding. Welding should be undertaken within the heat input range of 0.2-1.5 kJ/mm and with an interpass temperature of maximum 150°C (300°F).
Preheating or post-weld heat treatment is not necessary.
Matching filler metals are recommended in order to obtain a weld metal with optimum corrosion resistance and mechanical properties. For gas-shielded arc welding use Sandvik 25.10.4.L, and for manual metal-arc welding the covered electrode Sandvik 25.10.4.LR.
The values given below have been obtained by bending according to Swedish standard SS 11 26 26 method 3 (in a 90° V-block with a 25 mm die opening, a sample of 35 mm width, turned so that the burrs of the blanked edges face into the bend). They can be used as guidance for the smallest recommended bending radius.
|Tensile strength||Thickness||Min bending radius, mm|
// Parallel to the rolling direction
⊥ Transverse to the rolling direction
t is short for thickness
Sandvik SAF™ 2507 strip can be used in general strip applications where a good corrosion resistance is required. It is especially suitable for
- Seawater applications
- Chloride-containing bleaching environments in the pulp and paper industry
- Chemical industry
In the cold rolled condition Sandvik SAF™ 2507 is a very good spring material for corrosive environments.
In the annealed condition the combination of high yield strength and good corrosion resistance is inviting to a new design approach for a variety of applications. Especially allowing for non-corrosion protected light weight constructions with a low life cycle cost.