Sandvik 1C256 is a ferritic chromium steel for high-temperature applications. The grade is characterized by:
- Good resistance to reducing sulphurous gases
- Good resistance to oxidation in air
This steel can be used at temperatures up to 850°C (1560°F). However, allowance should be made for the low creep strength at the highest temperatures to avoid distortion due to the inherent mass of the steel.
EN Number: 1.4724**
- SEW 470
- EN 10095**
* Obsolete. Replaced by EN.
** Heat resisting steels and nickel alloys. Technical delivery conditions for sheet/plate, strip, bars, rods and sections.
Chemical composition (nominal)
- Heat exchangers for high-temperature applications
- Thermocouple protection tubes
- Injection nozzles
Sandvik 1C256 is highly resistant to oxidation, both at constant and at cyclically varying temperatures. The service temperature in air should not exceed about 850°C (1560°F).
Hot corrosion / sulphidation
Owing to its combined aluminium, silicon and chromium content and the absence of nickel, Sandvik 1C256 has a good resistance in sulphidizing gases.
Bending of tubes in Sandvik 1C256 can be carried out cold or hot. Annealing is not normally necessary after cold bending.
Hot-worked tubes should preferably be bent hot, but they can be bent cold, if the bending radii is greater than 5 times the diameter.
Hot bending is carried out at 900–800°C (1650–1470°F).
Forms of supply
Seamless tube and pipe in Sandvik 1C256 is supplied in dimensions up to 120 mm (4.72 in.) outside diameter in the annealed condition, but is also available white-pickled after annealing.
Tubes are delivered in the heat-treated condition. If another heat treatment is needed after further processing the following is recommended:
800–850°C (1470–1560°F), 10-30 minutes, rapid cooling in air.
800–860°C (1470–1580°F), 5-60 minutes, rapid cooling in air.
|Proof strength||Tensile strength||Elongation||Hardness|
1 MPa = 1 N/mm2
1) Rp0.2 and Rp1.0 correspond to 0.2% offset and 1.0% offset yield strength, respectively.
2) Based on L0 = 5.65 √S0, where L0 is the original gauge length and S0 the original cross-section area.
3) Hot finished products do not generally fulfill the min Rm requirement (450 MPa, 65 ksi) according to SEW 470.
Creep strength (approx. values)
|Temperature||Creep rupture strength, MPa|
|oC||10 000 h||100 000 h|
|Temperature||Creep rupture strength, ksi|
|ºF||10 000 h||100 000 h|
Since Sandvik 1C256 has very large creep-rupture elongation, often more than 100%, and little resistance to creep, it is necessary to allow for considerable creep deformation long before rupture occurs. At normal service temperatures, i.e. over 700°C (1290°F), even the mass of the tubes can cause stresses leading to extensive deformations.
Careful attention must, therefore, be given to the way in which the tubes are supported. Sandvik 1C256, in common with other ferritic chromium steels, is less tough than austenitic stainless steels in the as-delivered condition.
Density: 7.7 g/cm3, 0.28 lb/in3
|Temperature, °C||W/m °C||Temperature, °F||Btu/ft h °F|
|Temperature, °C||J/kg °C||Temperature, °F||Btu/lb °F|
|Temperature, °C||Per °C||Temperature, °F||Per °F|
1) mean values in temperature ranges x10-6
|Temperature, °C||MPa||Temperature, °F||ksi|
1) x 103
|Temperature, °C||μΩm||Temperature, °F||μΩin.|
The structural stability of Sandvik 1C256 is good, because of the low chromium content. Grain growth may be experienced at service temperatures above 900°C (1650°F).
The weldability of Sandvik 1C256 is good. Welding must be carried out with preheating at 200-300°C (390-570°F), subsequent heat treatment is normally required for matching filler metals. Suitable methods of fusion welding are manual metal-arc welding (MMA/SMAW) and gas-shielded arc welding, with the TIG/GTAW method as first choice.
For Sandvik 1C256, heat-input of <1.5 kJ/mm and interpass temperature of <150°C (300°F) are recommended.
Recommended filler metals
- ISO 14343 S 29 9 / AWS A5.9 ER312 (e.g. Exaton 29.9) or
- ISO 14343 S 25 20 / AWS A5.9 ER310 (e.g. Exaton 25.20.C) or
- ISO 18274 S Ni 6082 / AWS A5.14 ERNiCr-3 (e.g. Exaton Ni72HP)
- ISO 3581 E 29 9 R / AWS A5.4 E312-16 (e.g. Exaton 29.9.R) or
- ISO 3581 E 25 20 B / AWS A5.4 E310-16 (e.g. Exaton 25.20.B) or
- ISO 14172 E Ni 6182/ AWS A5.11 ENiCrFe-3 (e.g. Exaton Ni71)
When using the austenitic stainless-steel wire electrode S 25 20/ER310 and the covered electrode E 25 20 B/E310-16, the higher thermal expansion of the austenitic weld metal must be considered.
When using nickel alloy wire electrode S Ni 6082/ERNiCr-3 and covered electrode E Ni 6182/ENiCrFe-3, a lower corrosion resistance of the weld metal in a reducing sulphurous environment than the Sandvik 1C256 must be considered.