Piece hardening of Sandvik 12C27M knife steel

Need to know more?

Call us Email us

Austenitizing

Belt furnace. Time in furnace according to the table.

Thickness, mm Thickness, in Time, minutes
2.5 0.100 5
3.0 0.118 6
3.25 0.128 7
3.5 0.138 8
3.75 0.148 10
4.0 0.157 12
4.9 0.192 25

Quenching

Quench as rapidly as possible. For optimal results 600°C (1110°F) should be reached within 2 minutes or less.

Tempering (2 hours)
Hardness Temperature
58 HRC 175°C (345°F)
56 HRC 225°C (435°F)
53 HRC 350°C (660°F)