Sulphuric acid + chlorides

These corrosion data are mainly based on results of general corrosion laboratory tests, carried out with pure chemicals and water solutions nearly saturated with air (the corrosion rate can be quite different if the solution is free from oxygen).

All concentrations are given in weight-% and the solvent is water if nothing else is shown. The corrosion data apply to annealed materials with normal microstructure and clean surfaces, throughout.

Sulphuric acid + chlorides, (200 ppm CI-)
Conc.H2SO4%	1	1	1	1	5	5	5	10	10	10	10	10	20	20	20	20
Conc.Cl-ppm	200	200	200	200	200	200	200	200	200	200	200	200	200	200	200	200
Temp.°C	70	80	90	100	70	80	90	50	60	70	80	90	40	50	60	70
Grade or type of alloy:
Carbon steel
13 Cr
Alleima® 1802
Alleima® 3R12
Alleima® 3R60		0							1
18Cr13Ni3Mo ¹⁾
17Cr14Ni4Mo ²⁾
Alleima® 2RK65 ('904L')		0	1	1	0	2			0	0	2			0	1
Sanicro® 28					0	0	0	0	0			1	0	0	1	1
254 SMO	0	0	0	2	0	0	2		0	0	2	2		0		1
654 SMO							0
SAF™ 2304							2	2
SAF™ 2205								0	0			2	0	2	2	2
SAF™ 2507					0	0	0	0	0	0	0	2	0	0	0	0
SAF™ 2707 HD												0
SAF™ 2906												0
SAF™ 3207 HD												0
Ti

¹⁾ ASTM 317L, e.g. Alleima® 3R64
²⁾ EN 1.4439, e.g. Alleima® 3R68

Sulphuric acid + chlorides
Conc.H2SO4%	20	20	30	30	30	30	40	40	40	50	50
Conc.Cl-ppm	200	200	200	200	200	200	200	200	200	200	200
Temp.°C	80	90	30	40	50	60	15	25	40	50	60
Grade or type of alloy:
Carbon steel
13 Cr
Alleima® 1802
Alleima® 3R12
Alleima® 3R60			2
18Cr13Ni3Mo ¹⁾
17Cr14Ni4Mo ²⁾
Alleima® 2RK65 ('904L')	2		0	1		2	1	1
Sanicro® 28		1	0		1	1	0	0	0	0	0
254 SMO	1	2	0	1	1		0	0	0
654 SMO
SAF™ 2304
SAF™ 2205		2			2	2			2	0
SAF™ 2507		2						2	2
SAF™ 2707 HD								2
SAF™ 2906								2
SAF™ 3207 HD								1
Titanium (CP Ti)

¹⁾ ASTM 317L, e.g. Alleima® 3R64
²⁾ EN 1.4439, e.g. Alleima® 3R68

Sulphuric acid + chlorides
Conc.H2SO4%	1	1	1	1	3	3	5	5	5	5	5	5	10	10	10
Conc.Cl-ppm	2000	2000	2000	2000	2000	2000	2000	2000	2000	2000	2000	2000	2000	2000	2000
Temp.°C	70	80	90	100=BP	40	50	50	60	70	80	90	100	20	40	50
Grade or type of alloy:
Carbon steel
13 Cr
Alleima® 1802
Alleima® 3R12
Alleima® 3R60	0						1						0
18Cr13Ni3Mo ¹⁾
17Cr14Ni4Mo ²⁾
Alleima® 2RK65 ('904L')	0	1					0	1					0	0	1
Sanicro® 28	0				0	0	0	0	0				0	0	0
254 SMO	0	0	0				0	0	0				0	0	1
654 SMO	0	0	0	1			0	0	0	0	0		0	0	0
SAF™ 2304					0	0							1		2
SAF™ 2205													0	1
SAF™ 2507				1	0	0	0	0	0	0	0	2	0	0	0
SAF™ 2707 HD												0
SAF™ 2906												0
SAF™ 3207 HD												0
Titanium (CP Ti)

¹⁾ ASTM 317L, e.g. Alleima® 3R64
²⁾ EN 1.4439, e.g. Alleima® 3R68

Sulphuric acid + chlorides
Conc.H2SO4%	10	10	10	15	15	20	20	20	20	30	30	30	30	40	40
Conc.Cl-ppm	2000	2000	2000	2000	2000	2000	2000	2000	2000	2000	2000	2000	2000	2000	2000
Temp.°C	60	70	80	50	60	20	30	40	50	15	30	40	50	15	30
Grade or type of alloy:
Carbon steel
13 Cr
Alleima® 1802
Alleima® 3R12
Alleima® 3R60
18Cr13Ni3Mo ¹⁾
17Cr14Ni4Mo ²⁾
Alleima® 2RK65 ('904L')						0	1			1				1
Sanicro® 28						0	0	1		0
254 SMO						0	0			1				1
654 SMO	0	0	0	0	0	0	0	0	0	0	0	0	2	0	1
SAF™ 2304		2	2
SAF™ 2205
SAF™ 2507	0	1	2	1	2		1		2
SAF™ 2707 HD			0		0
SAF™ 2906			0		0
SAF™ 3207 HD			0		0				0
Titanium (CP Ti)

¹⁾ ASTM 317L, e.g. Alleima® 3R64
²⁾ EN 1.4439, e.g. Alleima® 3R68

Sulphuric acid + chlorides
Conc.H2SO4%	50	50	60	60	70	70	80	80	90	90	98	98
Conc.Cl-ppm	2000	2000	2000	2000	2000	2000	2000	2000	2000	2000	2000	2000
Temp.°C	15	30	15	30	15	30	15	30	15	30	15	30
Grade or type of alloy:
Carbon steel
13 Cr
Alleima® 1802
Alleima® 3R12
Alleima® 3R60
18Cr13Ni3Mo ¹⁾
17Cr14Ni4Mo ²⁾
Alleima® 2RK65 ('904L')	1		0		0	0	0	1	1		0	0
Sanicro® 28
254 SMO	1		1		0	1	0	1	1		1
654 SMO	1	1	1	1	0	1	0	0		2
SAF™ 2304
SAF™ 2205
SAF™ 2507
Titanium (CP Ti)

¹⁾ ASTM 317L, e.g. Alleima® 3R64
²⁾ EN 1.4439, e.g. Alleima® 3R68

Symbol clarification

These corrosion tables use a number of symbols, having the following meanings:

Symbol	Description
0	Corrosion rate less than 0.1 mm/year. The material is corrosion proof.
1	Corrosion rate 0.1—1.0 mm/year. The material is not corrosion proof, but useful in certain cases.
2	Corrosion rate over 1.0 mm/year. Serious corrosion. The material is not usable.
p, P	Risk (severe risk) of pitting and crevice corrosion.
c, C	Risk (Severe risk) of crevice corrosion. Used when there is a risk of localised corrosion only if crevices are present. Under more severe conditions, when there is also a risk of pitting corrosion, the symbols p or P are used instead.
s, S	Risk (Severe risk) of stress corrosion cracking.
ig	Risk of intergranular corrosion.
BP	Boiling solution.
ND	No data. (Used only where there are no actual data to estimate the risk of localised corrosion instead of p or s).

Disclaimer: Laboratory tests are not strictly comparable with actual service conditions. Accordingly, Alleima makes no warranties, express or implied, and accept no liability, compensatory or consequential, for the performance of different materials in individual applications that may be based on the information provided in this publication.