Sandvik 3R12 is an austenitic stainless chromium-nickel steel with a low carbon content.
ASTM: TP304L, TP304
UNS: S30403, S30400
EN Number: 1.4306, 1.4301
W.Nr.: 1.4306*, 1.4301*
DIN: X 2 CrNi 19 11*, X 5 CrNi 18 10*
SS: 2352*, 2333*
AFNOR: Z 2 CN 18.10*
BS: 304S31*, 304S11*
JIS: SUS304L, SUS304LTB, SUS304TP
- ASTM A213, A269 and A312
- JIS G3459
- JIS G3463
- EN 10216-5
- BS 3605, 3606*
- DIN 17456, 17458*
- NFA 49-117, 49-217
- SS 14 23 52, 14 23 33*
* Obsolete. Replaced by EN.
JIS approval for Stainless Steel Tubes
Chemical composition (nominal)
Subject to agreement, material with extra low Co content can be supplied.
Sandvik 3R12 is used for a wide range of industrial applications. Typical examples are: heat exchangers, condensers, pipelines, cooling and heating coils in the chemical, petrochemical, fertilizer, pulp and paper and nuclear power industries, as well as in the production of pharmaceuticals, foods and beverages.
Sandvik 3R12 has good resistance in
- Organic acids at moderate temperatures
- Salt solutions, e.g. sulfates, sulfides and sulfites
- Caustic solutions at moderate temperatures
Sandvik 3R12 has better resistance than normal type ASTM TP304 to oxidizing agents, such as nitric acid. Figure 2 shows isocorrosion in nitric acid for Sandvik 3R12.
Sandvik 3R12 has a low carbon content and therefore better resistance to intergranular corrosion than steels of type ASTM TP304.
The TTC-diagram, Figure 3, which shows the result of testing for 24 h in boiling Strauss solution (12% sulfuric acid, 6% copper sulfate) confirms the superior resistance of Sandvik 3R12. This is an advantage in complicated welding operations.
The good resistance against intergranular attack of Sandvik 3R12 is also demonstrated in the Huey test (boiling in 65% nitric acid for 5x48 h). A maximum corrosion rate of 0.40 mm/year in the annealed condition and 0.60 mm/year in the sensitized (675°C (1275oF)) condition can be met.
Sandvik 3R12 with its controlled and low impurity level, shows better results than ordinary ASTM TP304L or TP321.
Pitting and crevice corrosion
The steel may be sensitive to pitting and crevice corrosion even in solutions of relatively low chloride content. Molybdenum-alloyed steels have better resistance improves with increasing molybdenum content.
Stress corrosion cracking
Austenitic steels are susceptible to stress corrosion cracking (SCC). This may occur at temperatures above about 60°C (140°F) if the steel is subjected to tensile stresses and at the same time comes into contact with certain solutions, particularly those containing chlorides. Such service conditions should therefore be avoided. Conditions when plants are shut down must also be considered, as the condensates which are then formed can develop conditions that leads to both stress corrosion cracking (SCC) and pitting.
In applications demanding high resistance to stress corrosion cracking (SCC) we recommend the duplex (austenitic-ferritic) steel Sandvik SAF 2304.
Sandvik 3R12 can be used in:
- Air up to 850°C (1560°F)
- Steam up to 750°C (1380°F)
- Synthesis gas (ammonia synthesis) up to about 550°C (1020°F).
Creep behavior should also be taken into account when using the Sandvik 3R12 in the creep range.
In flue gases containing sulfur, the corrosion resistance is reduced. In such environments the steel can be used at temperatures up to 600-750°C (1110-1380°F) depending on service conditions. Factors to consider are whether the atmosphere is oxidizing or reducing, i.e. the oxygen content, and whether impurities such as sodium and vanadium are present.
Annealing after cold bending is not normally necessary, but this point must be decided with regard to the degree of bending and the operating conditions. Heat treatment, if any, should take the form of stress relieving or solution annealing, see under 'Heat treatment'.
Hot bending is carried out at 1100-850°C (2010-1560°F) and should be followed by solution annealing.
Forms of supply
Seamless tube and pipe in Sandvik 3R12 is supplied in dimensions up to 260 mm (10.2 in.) outside diameter in the solution-annealed and white-pickled condition or solution annealed by a bright-annealing process. U-bent tubes can be supplied on request.
Tubes in Sandvik 3R12 are normally delivered in heat treated condition. If additional heat treatment is needed after further processing the following is recommended.
850-950°C (1560-1740°F), cooling in air.
1000-1100°C (1830-2010°F), rapid cooling in air or water.
For tube and pipe with wall thickness greater than 10 mm (0.4 in.) the proof strength may fall short of the stated value by about 10 MPa (1.4 ksi).
1 MPa = 1 N/mm2
a) Rp0.2 and Rp1.0 correspond to 0.2% offset and 1.0% offset yield strength, respectively.
b) Based on L0 = 5.65 √S0 where L0 is the original gauge length and S0 the original cross-section area.
Due to its austenitic microstructure, Sandvik 3R12 has very good impact strength, both at room temperature and at cryogenic temperatures.
Tests have demonstrated that the grade fulfils the requirements according to the European standards EN 13445-2 (UFPV-2) ( (min. 60 J (44 ft-lb) at -270 oC (-455 oF)) and EN 10216-5 (min. 60 J (44 ft-lb) at -196 oC (-320oF).
||10 000 h
||100 000 h
Density: 7.9 g/cm3, 0.29 lb/in3
|Temperature, °C||W/m °C||Temperature, °F||Btu/ft h °F|
|Temperature, °C||J/kg °C||Temperature, °F||Btu/lb °F|
|Temperature, °C||Per °C||Temperature, °F||Per °F|
1) Mean values in temperature ranges (x10-6)
|Temperature, °C||MPa||Temperature, °F||ksi|
1) Modulus of elasticity, (x103)
The weldability of Sandvik 3R12 is good. Welding must be carried out without preheating and subsequent heat treatment is normally not required. Suitable methods of fusion welding are manual metal-arc welding (MMA/SMAW) and gas-shielded arc welding, with the TIG/GTAW method as first choice.
For Sandvik 3R12, heat input of <2.0 kJ/mm and interpass temperature of <150°C (300°F) are recommended.
Recommended filler metals
TIG/GTAW or MIG/GMAW welding
ISO 14343 S 19 9 L / AWS A5.9 ER308L (e.g. Exaton 19.9.L)
ISO 3581 E 19 9 L R / AWS A5.4 E308L-17(e.g. Exaton 19.9.LR)
ISO 14343 S 19 9 L / AWS A5.9 ER308L (e.g. Exaton 19.9.L) wire or strip electrodes are recommended for overlay welding of tube sheets and high-pressure vessels in cases where corrosion resistance, equal to that of Sandvik 3R12, is required.